11.8不锈钢成分技术条件
不锈钢成分技术条件
不锈钢成分技术条件见表3.1-43。
表3.1-43 不锈钢成分技术条件(摘自ISO 683-13:1986)
钢的类型① | 化学成分②/% | 化学成分 | 紧固件组别标记④ | ||||||||||||
C | Si | Mn | P | s | N | A1 | Cr | Mo | Nb③ | Ni | Se | Ti | Cu | ||
max | max | max | min | ||||||||||||
铁素体钢 | |||||||||||||||
8 | 0.08max | 1.0 | 1.0 | 0.040 | 0.030max | — | — | 16.0-18.0 | — | — | 1 .0max | — | — | — | F1 |
8b | 0.07max | 1.0 | 1.0 | 0.040 | 0.030max | — | — | 16.0-18.0 | — | — | 1 .0max | — | 7x%C≤1.10 | — | F1 |
9c | 0.08max | 1.0 | 1.0 | 0.040 | 0.030max | — | — | 16.0-18.0 | 0.90-1.30 | — | 1 .0max | — | — | — | F1 |
F1 | 0.025max⑤ | 1.0 | 1.0 | 0.040 | 0.030max | 0.025max⑤ | — | 17.0-19.0 | 1.75-2.50 | —⑥ | 0.60max | — | —⑥ | — | F1 |
马氏体钢 | |||||||||||||||
3 | 0.09-0.15 | 1.0 | 1.0 | 0.040 | 0.030max | — | — | 11.5-13.5 | — | — | 1 .0max | — | — | — | Cl |
7 | 0.08-0.15 | 1.0 | 1.5 | 0.060 | 0.15-0.35 | — | — | 12.0-14.0 | 0.60max⑦ | — | 1 .0max | — | — | — | C4 |
4 | 0.16-0.25 | 1.0 | 1.0 | 0.040 | 0.030max | — | — | 12.0-14.0 | — | — | 1 .0max | — | — | — | Cl |
9a | 0.10-0.17 | 1.0 | 1.5 | 0.060 | 0.15-0.34 | — | — | 15.5-17.5 | 0.60max⑦ | — | 1 .0max | — | — | — | C3 |
9b | 0.14-0.23 | 1.0 | 1.0 | 0.040 | 0.030max | — | — | 15.0-17.5 | — | — | 1.5-2.5 | — | — | — | C3 |
5 | 0.26-0.35 | 1.0 | 1.0 | 0.040 | 0.030max | — | — | 12.0-14.0 | — | — | 1 .0max | — | — | — | Cl |
奥氏体钢 | |||||||||||||||
10 | 0.030raax | 1.0 | 2.0 | 0.045 | 0.030max | — | — | 17.0-19.0 | — | — | 9.0-12.0 | — | — | — | A2⑧ |
11 | 0.07max | 1.0 | 2.0 | 0.045 | 0.030raax | — | — | 17.0-19.0 | — | — | 8.0-11.0 | — | — | — | A2 |
15 | 0.08max | 1.0 | 2.0 | 0.045 | 0.030max | — | — | 17.0-19.0 | — | — | 9.0-12.0 | — | 5x%C≤0.80 | — | A3⑨ |
16 | 0.08max | 1.0 | 2.0 | 0.045 | 0.030max | — | — | 17.0-19.0 | — | 10x%C ≤1.0 | 9.0-12.0 | — | — | — | A3⑨ |
17 | 0.12max | 1.0 | 2.0 | 0.06 | 0.15-0.35 | — | — | 17.0-19.0 | —⑩ | — | 8.0-10.0⑪ | — | — | — | A1 |
13 | 0. l0max | 1.0 | 2.0 | 0.045 | 0.030max | — | — | 17.0-19.0 | — | — | 11.0-13.0 | — | — | — | A2 |
19 | 0.030max | 1.0 | 2.0 | 0.045 | 0.030max | — | — | 16.5-18.5 | 2.0-2.5 | — | 11.0-14.0 | — | — | — | A4 |
20 | 0.07max | 1.0 | 2.0 | 0.045 | 0.030max | — | — | 16.5 -18.5 | 2.0-2.5 | — | 10.5-13.5 | — | — | — | A4 |
21 | 0.08max | 1.0 | 2.0 | 0.045 | 0.030max | — | — | 16.5-18.5 | 2.0-2.5 | — | 11.0-14.0 | — | 5x%C≤0.80 | — | A5⑨ |
23 | 0.08max | 1.0 | 2.0 | 0.045 | 0.030max | — | — | 16.5-18.5 | 2.0-2.5 | 10x%C≤1.0 | 11.0-14.0 | — | — | A5⑨ | |
19a | 0.030max | 1.0 | 2.0 | 0.045 | 0.030max | — | — | 16.5-18.5 | 2.5-3.0 | — | 11.5-14.5 | — | — | — | A4 |
20a | 0.07max | 1.0 | 2.0 | 0.045 | 0.030max | — | — | 16.5- 18.5 | 2.5-3.0 | — | 11.0-14.0 | — | — | — | A4 |
10N | 0.030max | 1.0 | 2.0 | 0.045 | 0.030max | 0.12-0.22 | — | 17.0-19.0 | — | — | 8.5-11.5 | — | — | — | A2 |
19N | 0.030max | 1.0 | 2.0 | 0.045 | 0.030max | 0.12-0.22 | — | 16.5-18.5 | 2.0-2.5 | — | 10.5-13.5 | — | — | — | A4⑧ |
19aN | 0.030max | 1.0 | 2.0 | 0.045 | 0.030max | 0.12-0.22 | — | 16.5-18.5 | 2.5-3.0 | — | 11.5-14.5 | — | — | — | A4⑧ |
①类型编号是暂定的,当制定有关的国际标准时,还会改变。
②本表未列出的元素,未经用户同意,不能增加,除非需要精炼。应采取合理的预防措施,以防止某些元素(来自制造过程中混入的废料或其他金属)的增加,因为这些元素会影响材料的淬透性、机械性能和使用性能。
③钽含量取决于铌含量。
④不是ISO 683-13的内容。
⑤(C + N)max为0.040%。
⑥8x(C + N)≤(Nb + Ti)≤0.80%。
⑦在询问和签约订单之后,可能提供Mo含量为0.20%〜0.60%的钢。
⑧有极好的耐晶间腐蚀性。
⑨稳定型钢。
⑩制造者可选择添加最大到0.70%的钼。
⑪对制造无缝钢管的半成品,镍含量可能增加0.5%。