11.9冷镦和冷挤压用不锈钢
冷镦和冷挤压用不锈钢
冷镦和冷挤压用不锈钢见表3.1-44。
表3.1-44冷镦和冷挤压用不锈钢（摘自IS04954:1993)
| 钢的类型（标记①) | 化学成分 | 化学成分©/% | 紧固件③组别标记 | |||||||||
| No. | 名 称 | ISO 4954：1979 | C | Si | Mn | P | S | Cr | Mo | Ni | 其他 | |
| max | max | max | max | |||||||||
| 铁素体钢 | ||||||||||||
| 71 | X3Cr17E | — | ≤0.04 | 1.0 | 1.0 | 0.04 | 0.03 | 16.0-18.0 | ≤1.0 | F1 | ||
| 72 | X6Cr17E | D1 | ≤0.08 | 1.0 | 1.0 | 0.04 | 0.03 | 16.0-18.0 | ≤1.0 | F1 | ||
| 73 | X6CrMol7 1E | D2 | ≤0.08 | 1.0 | 1.0 | 0.04 | 0.03 | 16.0-18.0 | ≤1.0 | F1 | ||
| 74 | X6CrTil2E | — | ≤0.08 | 1.0 | 1.0 | 0.04 | 0.03 | 10.5-12.5 | 0.90-1.30 | ≤0.50 | Ti：6x%C≤1.0 | F1 |
| 75 | X6CrNbl2E | — | ≤0.08 | 1.0 | 1.0 | 0.04 | 0.03 | 10.5-12.5 | ≤0.50 | Ti：6x%C≤1.0 | F1 | |
| 马氏体钢 | ||||||||||||
| 76 | X12Cr13E | D10 | 0.90-0.15 | 1.0 | 1.0 | 0.04 | 0.03 | 11.5-13.5 | ≤1.0 | Cl | ||
| 77 | X19CrNil6 2E | D12 | 0.14-0.23 | 1.0 | 1.0 | 0.04 | 0.03 | 15.0-17.5 | 1.5-2.5 | C3 | ||
| 奥氏体钢 | ||||||||||||
| 78 | X2CrNil8 10E | D20 | ≤0.030 | 1.0 | 2.0 | 0.045 | 0.03 | 17.0-19.0 | 9.0-12.0 | A2④ | ||
| 79 | X5CrNil8 9E | D21 | ≤0.07 | 1.0 | 2.0 | 0.045 | 0.03 | 17.0-19.0 | 8.0-11.0 | A2 | ||
| 80 | X10CrNil8 9E | D22 | ≤0.12 | 1.0 | 2.0 | 0.045 | 0.03 | 17.0-19.0 | 8.0-10.0 | A2 | ||
| 81 | X5CrNil8 12E | D23 | ≤0.07 | 1.0 | 2.0 | 0.045 | 0.03 | 17.0-19.0 | 11.0-13.0 | A2 | ||
| 82 | X6CrNil8 16E | D25 | ≤0.08 | 1.0 | 2.0 | 0.045 | 0.03 | 15.0-17.0 | 17.0-19.0 | A2 | ||
| 83 | X6CrNiTil8 10E | D26 | ≤0.08 | 1.0 | 2.0 | 0.045 | 0.03 | 17.0-19.0 | 9.0-12.0 | Ti：5x%C≤0.80 | A3 | |
| 84 | X5CrNiMo17 12 2E | D29 | ≤0.07 | 1.0 | 2.0 | 0.045 | 0.03 | 16.5-18.5 | 2.0-2.5 | 10.5-13.5 | A4 | |
| 85 | X6CrNiMoTil7 12 2E | D30 | ≤0.06 | 1.0 | 2.0 | 0.045 | 0.03 | 16.5-18.5 | 2.0-2.5 | 11.0-14.0 | Ti：5x%C≤0.80 | A5 |
| 86 | X2CrNiMol7 13 3E | — | ≤0.030 | 1.0 | 2.0 | 0.045 | 0.03 | 16.5-18.5 | 2.5-3.0 | 11.5-14.5 | A4④ | |
| 87 | X2CrNiMoN17 13 3E | — | ≤0.030 | 1.0 | 2.0 | 0.045 | 0.03 | 16.5-18.5 | 2.5-3.0 | 11.5-14.5 | N:0.12- 0.22 | A4④ |
| 88 | X3CrNiCul8 9 3E | D32 | ≤0.04 | 1.0 | 2.0 | 0.045 | 0.03 | 17.0-19.0 | 8.5 ~ 10.5 | Cu:3.00- 4.00 | A2 | |
①第1列的标记是顺序编号。第2列的标记是根据ISO/TC17/SC2建议的标记制度。第3列的标记表示在ISO 4954: 1979 (1993修订）使用并 已作废的编号。
②本表未列出的元素，未经用户同意，不能增加，除非需要精炼。应采取合理的预防措施，以防止某些元素（来自制造过程中混入的废料或其他金属）的增加，因为这些元素会影响材料的淬透性、机械性能和使用性能。
③不是ISO 4954的内容。
④有极好的耐晶间腐蚀性。